Harris® Stay Brite® SB31 Solder, 1 lb, Spool
Brand: Harris®
Item No: 10004
Sign In for Availability
Description
Stay Brite solders bond with all of the ferrous and nonferrous alloys. Joints soldered with Stay Brite solders exhibit considerably higher than necessary elongation for sound, dissimilar metal joints and vibration applications. Both Stay Brite and Stay Brite 8 produce an overall component with greater strength than a brazed component whose base metals are weakened by annealment from high brazing heat.
Harris® Solder, 1 lb Net Content, Spool Container, Composition: 96% Tin, 4% Silver, 1/8 in Wire Diameter, 430 deg F Melting Point, 10600 psi Shear Strength, 14000 psi Tensile Strength, 16.4 Electrical Conductivity
Features
- Industry standard solder for HVAC connections
- Engineered to provide strong, ductile connections on copper, brass, steel and stainless steel
- Silver color is a good color match to stainless steel
- The low temperature/rapid melting characteristic promotes capillary flow and less base metal distortion and oxidation
- Ideal for very tight connections
- Meets NSF/ANSI Standard 51 for food eqiupment materials
- Meets NSF/ANSI Standard 61 for drinking water system components - health effects
- Meets NSF/ANSI Standard 372 for drinking water system components - lead content
- Conforms to the EU Reach & RoHS directive
Specifications
|
Alloy Type |
Solder |
|
Chemical Composition |
Silver 3.4-3.8%Tin Remainder% |
|
Color |
Silver (as deposited) |
|
Composition |
96% Tin, 4% Silver |
|
Container Type |
Spool |
|
Density |
.271 (lbs./cu.in.) |
|
Diameter |
1/16" (1.59mm) |
|
Electrical Conductivity (%IACS) |
16.4 |
|
Electrical Conductivity |
16.4 |
|
Liquidus |
430 deg F (221 deg C) |
|
Melting Point |
430 deg F |
|
ModelName |
STAY BRITE® Solder |
|
Net Content |
1 lb |
|
Recommended Flux |
Harris Stay-Clean paste flux and Harris Bridgit Burn Resistant paste flux are good choices for soldering copper and brass. For copper tube plumbing applications Bridgit Water Soluble flux may also be used. For soldering steel or stainless steel Harris Stay-Clean liquid flux is recommended. Stay-Clean liquid is an active flux that provides improved oxide removal and protection hen soldering ferrous metals. Remove flux residue upon completion. |
|
Shear Strength (PSI) |
10,600 (copper lap joint) |
|
Shear Strength |
10600 psi |
|
Size |
1 lb. spool |
|
Solidus |
430 deg F (221 deg C) |
|
Tensile Strength |
14000 psi |
|
Wire Diameter |
1/8 in |
Documentation